浸渍碳石墨技术技能
浸渍碳石墨技术技能
|
类别 |
型号 |
抗压强度≥Mpa |
抗折强度≥Mpa |
肖氏强度≥Mpa |
气孔率 |
体积密度g/cm3 |
使用温度℃ |
|
碳石墨 |
HMC-201 |
50 |
30 |
40 |
15 |
1.6 |
350 |
|
HMC-202 |
60 |
30 |
45 |
20 |
1.60 |
350 |
|
|
HMC-203 |
62 |
35 |
45 |
18 |
1.65 |
400 |
|
|
HMC-204 |
70 |
35 |
55 |
15 |
1.65 |
400 |
|
|
HMC-205 |
80 |
38 |
60 |
20 |
1.70 |
450 |
|
|
HMC-206 |
56 |
25 |
50 |
20 |
1.72 |
450 |
|
|
HMC-207 |
65 |
35 |
55 |
20 |
1.72 |
500 |
|
|
HMC-208 |
78 |
36 |
62 |
12 |
1.80 |
500 |
|
|
浸渍酚醛树脂 |
HMC-202F |
100 |
50 |
70 |
1.5 |
1.70 |
180 |
|
HMC-203F |
110 |
55 |
76 |
1.2 |
1.72 |
180 |
|
|
HMC-205F |
176 |
60 |
85 |
1 |
1.85 |
180 |
|
|
HMC-208F |
160 |
60 |
75 |
1 |
1.85 |
180 |
|
|
浸渍呋喃树脂 |
HMC-203K |
100 |
55 |
70 |
1.3 |
1.72 |
200 |
|
HMC-205K |
170 |
60 |
82 |
1 |
1.85 |
200 |
|
|
HMC-208K |
150 |
60 |
76 |
1 |
1.85 |
200 |
|
|
浸渍环氧树脂 |
HMC-203H |
100 |
57 |
70 |
1.5 |
1.72 |
200 |
|
HMC-205H |
168 |
60 |
82 |
1.2 |
1.85 |
200 |
|
|
HMC-208H |
150 |
60 |
76 |
1.2 |
1.86 |
200 |
|
|
浸渍聚 |
HMC-202F4 |
90 |
60 |
66 |
1.2 |
1.70 |
260 |
|
HMC-203F4 |
100 |
65 |
70 |
1.2 |
1.72 |
260 |
|
|
HMC-205F4 |
170 |
70 |
80 |
1 |
1.85 |
260 |
|
|
HMC-208F4 |
150 |
70 |
72 |
1 |
1.85 |
260 |
|
|
浸渍巴氏合金 |
HMC-203B |
110 |
50 |
80 |
3 |
2.30 |
220 |
|
HMC-205B |
180 |
55 |
85 |
3 |
2.30 |
220 |
|
|
浸渍锑合金 |
HMC-203D |
130 |
55 |
90 |
2.8 |
5.00 |
450 |
|
HMC-205D |
185 |
60 |
100 |
2.8 |
5.00 |
450 |
|
|
浸渍铜合金 |
HMC-203C |
120 |
55 |
90 |
2.5 |
5.50 |
400 |
|
HMC-205C |
185 |
60 |
100 |
2.5 |
5.50 |
400 |